NEITABOND Mirror-faced panel is made by doing an anodic oxidation on the aluminum surface to make the product surface as bright as a mirror. It is safer to apply and easier to process into various shapes than glass materials. This technique does not only exhibit the unique surface effect of the natural essential color of aluminum, but also equips the product with a combined appearance of the modern and the classical, now mirror panels are widely used in the interior decoration.
Mirror aluminum composite panel is a new composite material skinned with anodized aluminum mirror sheets. The lower aluminum skin is chromate treated and polyester coated. It has silver and gold mirror finishing, and now more colors for choices, such as other vivid colors.
Soft white or bright red? Solid colours are always a good choice when a uniform appearance without special effects is required.
High resistance to peeling
Superior weather resistance
Light weight and easy to process
Coating evenness
Diversified colors
Easy for maintenance
Impact resistance
| Aluminum alloy | AA1100 series |
| Aluminum skin | 0.21mm,0.30mm,0.40mm,0.5mm |
| Panel thickness | 3mm,4mm |
| Panel width | 1220mm,1250mm,1500mm |
| Panel length | 2440mm,3050mm,4050mm |
| Surface treatment | Pre-anodized |
| Glossy | 40%-60% |
Panel width: ±2mm
Panel length:±3mm
Panel thickness: ±0.2mm
Panel diagonal: ≤5mm
Aluminum sheet thickness: ±0.02mm
| Description | Test standard | Polyester |
| Thickness of coating | Polyester paint >=16um | 16um to 18um |
| Coating flexibility (T-bend) | Polyester paint≥3T | 3T |
| Color different | ΔE≦2.0(follow color sample) | ΔE≦2.0 |
| Pencil hardness | ≧HB | ≧2H |
| Chemical resistance | 2%HCI or 2%NaOH test in 24 hours -No change | No change |
| Coating adhesion | ≧1grade for 10810mm2gridding test | 1grade |
| Resist solvent | 100times with Dimethylebnzene without change | No change |
| Boiling water resistance | 2 hours without change | No change |
| Peeling strength/stripping strength | Average ≧5N/mm of 180oc peel off for panel with 0.21mm alu.skin | 5N/mm |
| Impact test for paint | 20KG.cm impact-paint no split for panel | No split |
| Abrasion resistance (L/Mil) | NIL | NIL |
| Temperature resistance | -40℃ to +80℃ temperature without change of color difference and paint peel off,peeling strength average dropprate≦10% | Change of glossy only,no paint |
| Peel off | ||
| Cofficient of linear Thermal Expansion | 100℃ temperature difference | 2.4mm/n |
| Detergent resistance (3%) | ASTM D2248 | No change |
Humidity Resistance (3000hrs,100%RH,100°F) | ASTM D2247 | No change |
Salt spray resistance (3000hrs,5% salt) | ASTM B117 | No change |
| Resistance to Staining | 600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference ≦4.0 | No change |
The company possesses production lines for aluminum-plastic panels whose annual output is 520 million square meters.
Address：Zhongwei Road, Zhubao Industrial Zone, Lanshan District, Linyi City,Shandong China
E-mail：sales@neitabond.com
Tel：+86-539-3595209
Fax：+86-539-359520
Cell：+86-13583916866
Espacio Riesco, Santiago, ChileBOOTH
30th Jul.2019EXHIBITION: SIGN CHINA 2019 • SHANGHAI
29th Jul.2019EXHIBITION:THE 26TH SHANGHAI INT'LAD &SIGN TECHNOLOGY&EQUIPMENT EXHIBITION
01st Mar.2018
Linyi city Xingda Plastic Decoration Material Co.,Ltd. All Rights Reserved. Powered by HiCheng