Thickness of coating 

Polyester paint >=16um

16um to 18um

Coating flexibility (T-bend)

Polyester paint≥3T

3T

Color different 

ΔE≦2.0(follow color sample)

ΔE≦2.0

Pencil hardness

≧HB

≧2H

Chemical resistance 

2%HCI or 2%NaOH test in 24 hours -No change 

No change 

Coating adhesion

≧1grade for 10810mm2gridding test

1grade

Resist solvent 

100times with Dimethylebnzene without change

No change 

Boiling water resistance 

2 hours without change 

No change 

Peeling strength/stripping strength 

Average ≧5N/mm of 180oc peel off

 for panel with 0.21mm alu.skin

5N/mm

Impact test for paint 

20KGNaN impact-paint no split for panel 

No split 

Abrasion resistance (L/Mil)

NIL

NIL

Temperature resistance 

-40℃ to +80℃ temperature without 

change of color difference

 and paint peel off,peeling 

strength average dropprate≦10% 

Change of glossy only,no paint 

Peel off

Cofficient of linear Thermal Expansion 

100℃ temperature difference 

2.4mm/n

Detergent resistance (3%)

ASTM D2248

No change 

Humidity Resistance (3000hrs,100%RH,100°F)

ASTM D2247

No change 

Salt spray resistance (3000hrs,5% salt)

ASTM B117

No change 

Resistance to Staining 

600h radiate in 800W/M2 in humidity condition

,glossiness deviation less grade 2,color difference ≦4.0

No change